Hydrogen sulfide scavenger

ABSTRACT

The present disclosure is related to a family of metals chelates for use as a hydrogen sulfide scavenger in asphalt, and the preparation thereof. The metal chelates, in particular amino acid metal chelates, are particularly efficient at reducing the hydrogen sulfide emissions of asphalt.

CROSS REFERENCE TO RELATED APPLICATIONS

The present application is a continuation-in-part of U.S. Ser. No. 14/170,224, filed Jan. 31, 2014, the entire contents of which is hereby incorporated by reference.

FIELD OF THE INVENTION

The present disclosure relates to a hydrogen sulfide scavenger for use as an additive in asphalt.

BACKGROUND OF THE INVENTION

Asphalt is commonly used in the construction and paving of roads. Asphalt is a mixture of aggregate material, such as sand, gravel, and crushed stone, with hot bitumen. The bitumen coats the aggregate material to give the asphalt, which may be spread as a uniform layer upon a road bed and compacted and smoothed with heavy rolling equipment.

Asphalt invariably contains sulfur. The amount of sulfur will depend on the origin of the crude oil, as well as the processes used to refine the crude oil, into asphalt. The sulfur may exist in different forms. For example, sulfur may be in the form of hydrogen sulfide. Hydrogen sulfide, or dihydrogen sulfide, is a chemical compound with the formula H₂S. It is a colorless, poisonous, flammable gas with the characteristic foul odor.

Hydrogen sulfide may be released form asphalt, in particular when the asphalt is heated to a certain temperature. For example, hydrogen sulfide results from the dehydrogenation reactions that occur between bitumen and sulfur at the hot mixing temperatures, e.g. temperatures greater than 140° C. Hydrogen sulfide emissions are regulated. Therefore, there exists a need to reduce the amount of hydrogen sulfide in asphalt. Accordingly, the present disclosure provides for a reduced or low release of hydrogen sulfide during the preparation of asphalt, as well as in the final asphalt material.

SUMMARY OF THE INVENTION

The present disclosure is related to a family of metals chelates for use as a hydrogen sulfide scavenger in asphalt, and the preparation thereof. The metal chelates, in particular amino acid metal chelates, are particularly efficient at reducing the hydrogen sulfide emissions of asphalt.

The present disclosure is directed to a composition comprising asphalt and an amino acid metal chelate. In some embodiments, the amino acid metal chelate is selected from the group consisting of copper bis-glycinate, zinc bis-glycinate and mixtures thereof.

The present disclosure is also directed to a method of reducing hydrogen sulfide emission from asphalt, or the preparation thereof, comprising the step of combining an amino acid metal chelate to asphalt, or an asphalt mix. In some embodiments, the amino acid metal chelate is selected from the group consisting of copper bis-glycinate, zinc bis-glycinate and mixtures thereof.

The amino acid metal chelate may also be selected form the following: Boron Amino Acid Chelate; Boron Aspartate; Boron Citrate; Boron Glycinate; Calcium Alphaketoglutarate; Calcium Amino Acid Chelate; Calcium Arginate; Calcium Ascorbate; Calcium Aspartate; Calcium Caprylate; Calcium Carbonate; Calcium Citrate Malate; Calcium Glycinate; Calcium D-Glucarate; Calcium Krebs Cycle; Calcium Lactate; Calcium Malate; Calcium Orotate; Calcium Succinate; Chromium Amino Acid Chelate; Chromium Arginate; Chromium Chloride; Chromium Dinicotinate/Glycinate; Chromium Picolinate; Chromium Nicotinate; Chromium Trit; Chromium Yeast; Chromium Nicotinate/Glycinate; Copper Amino Acid Chelate; Copper Aspartate; Copper Carbonate; Copper Citrate; Copper Gluconate; Copper Glycinate; Copper Sulfate; Copper Yeast; Iron Amino Acid Chelate; Iron Aspartate; Iron Bis-Glycinate HCl Soluble; Iron Citrate; Iron Fumarate; Iron Gluconate; Iron Glycinate; Iron Sulfate; Iron Yeast; Lithium Aspartate; Lithium Orotate; Magnesium Alphaketoglutarate; Magnesium Amino Acid Chelate; Magnesium Ascorbate; Magnesium Aspartate; Magnesium Citrate; Magnesium Gluconate; Magnesium Glycinate; Magnesium Malate; Magnesium Orotate; Magnesium Oxide; Magnesium Succinate; Magnesium Taurinate; Magnesium Yeast; Manganese Amino Acid Chelate; Manganese Aspartate; Manganese Carbonate; Manganese Citrate; Manganese Gluconate; Mananese Glycinate; Manganese Sulfate; Manganese Yeast; Molybdenum Amino Acid Chelate; Molybdenum Trit; Molybdenum Yeast; Sodium Molybdate; Phosphorus Amino Acid Chelate; Dicalcium Phosphate; Potassium Amino Acid Chelate; Potassium Ascorbate; Potassium Aspartate; Potassium Citrate; Potassium Chloride; Potassium D-Glucarate; Potassium Gluconate; Potassium Glycerophosphate; Potassium Iodide Trit; Potassium Succinate; Selenium Amino Acid Chelate; Selenium Aspartate; L-Selenomethionine; Selenium Yeast; Sodium Selenate; Sodium Selenite; Strontium Aspartate; Strontium Citrate; Strontium Glycinate; Vanadium Amino Acid Chelate; Vanadium Citrate; Bis-Maltolato Oxo Vanadium; Vanadyl Sulfate; Sodium Metavanadate; Zinc Acetate; Zinc Arginate; Zinc Amino Acid Chelate; Zinc Ascorbate; Zinc Aspartate; Zinc Gluconate; Zinc Glycinate; Zinc Methionate; Zinc Oxide; Zinc Picolinate; Zinc Sulfate; and Zinc Yeast and mixtures thereof.

Said amino acid metal chelates can be added to the asphalt as a liquid (e.g a solvent), solid, powder, slurry, gel, or emulsion.

Applicant has discovered that when a solid amino acid metal chelate H₂S scavenger is dispersed in a solvent such as glycerol, kerosene, naphta, aliphatic, aromatic or naphthenic oil or any solvent with a flash point compatible with asphalt or bitumen, said solvent dispersion will provide similar performance to the solid form of said scavenger in the presence or not of polyphosphoric acid or other typical additives used in asphalt. In addition the liquid scavenger is stable overtime in normal storage conditions.

The preparation of the liquid scavenger follow typically the steps below:

-   -   The solvent is maintain at room temperature or heated up to a         temperature below the flash point of the considered solvent     -   Some suspension stabilizers, thinner or thickener agent could be         used to improve the stability of the mixture     -   The addition of the solid scavenger under agitation typically         for 15 minutes to 10 hours. The concentration of the solid         scavenger varies according to the workability of the mixture,         and typically could range from 5% wt to 90% and most typically         from 20 to 60% wt.

The rate of addition into the asphalt or bitumen is proportionel to its solid content and varies from 0.05 to 5%, preferably from 0.1 to 0.5% wt.

The following example illustrates the neutral impact in terms of performance grading of the addition of the liquid form of the scavenger into asphalt.

ODSR Sample (° C.) Neat Bitumen A 58-28 58.0 Neat A + 1% polyphosphoric 65.6 acid-Control Neat A + 0.2% Liquid 65.4 Scavenger + 1% PPA Neat A + 0.2% Liquid 64.8 Scavenger + 1% PPA Neat Bitumen B 58-28 58.7 Neat B + 1% PPA - Control 66.0 Neat B + 0.2% Liquid 65.8 Scavenger + 1% PPA Neat B + 0.2% Liquid 65.6 Scavenger + 1% PPA Neat Bitumen C 58-28 59.8 Neat C + 1% PPA - Control 67.0 Neat C + 0.2% Liquid 66.4 Scavenger + 1% PPA Neat C + 0.2% Liquid 66.5 Scavenger + 1% PPA Original Dynamic Shear Rheometer (ODSR)

EXAMPLE Example 1

Hydrogen sulfide emissions were measured from asphalt samples containing an amino acid metal chelate versus a control containing no amino acid metal chelate. Three asphalt samples were prepared and their hydrogen sulfide emissions measured after 1 hour in storage. To two samples, 0.5% amino acid metal chelate additive was added, CuGlyc (copper bis-glycinate) and ZnGlyc (zinc bis-glycinate) respectively. The hydrogen sulfide emissions were measured again after 5 minutes and 1 hour. Table 1 lists the results. The addition of the amino acid metal chelate showed significant reduction in hydrogen sulfide emissions.

TABLE 1 Hydrogen Sulfide Emission H₂S (ppm) H₂S (ppm) H₂S (ppm) 5 minutes 1 hour after Storage at after adding 160, one addition of scavenger % Additive Temp hour scavenger material 0 Control 180° C. 16 10 0.5 CuGlyc 180° C. 12 4 1 0.5 ZnGlyc 180° C. 10 5 1

Example 2

Additional amino acid metal chelates that may be used in asphalt, or the preparation thereof, are listed in Table 2.

TABLE 2 Amino Acid Metal Chelates Metal Chelating agent Chromium Amino Acid Arginate Chloride Dinicotinate/Glycinate Picolinate Nicotinate TritChromium Yeast Copper Amino Acid Aspartate Carbonate Citrate Gluconate Sulfate Yeast Iron Amino Acid Aspartate Bis-Glycinate Citrate Fumarate Gluconate Sulfate Yeast Manganese Amino Acid Aspartate Carbonate Citrate Gluconate Sulfate Yeast Molybdenum Amino Acid TritMolybdenum Yeast Sodium Molybdate Selenium Amino Acid Aspartate L-Selenomethionine Yeast Sodium Selenate Sodium Selenite Strontium Aspartate Citrate Glycinate Vanadium Amino Acid Citrate Bis-Maltolato Oxo Vanadium Vanadyl Sulfate Sodium Metavanadate Zinc Acetate Arginate Amino Acid Ascorbate Aspartate Gluconate Glycinate Methionate Picolinate Sulfate Yeast 

What is claimed is:
 1. A composition comprising: (i) asphalt or an asphalt mix, and (ii) an amino acid metal chelate.
 2. The composition of claim 1, wherein the amino acid metal chelate is selected from the group consisting of Boron Amino Acid Chelate; Boron Aspartate; Boron Citrate; Boron Glycinate; Calcium Alphaketoglutarate; Calcium Amino Acid Chelate; Calcium Arginate; Calcium Ascorbate; Calcium Aspartate; Calcium Caprylate; Calcium Carbonate; Calcium Citrate Malate; Calcium Glycinate; Calcium D-Glucarate; Calcium Krebs Cycle; Calcium Lactate; Calcium Malate; Calcium Orotate; Calcium Succinate; Chromium Amino Acid Chelate; Chromium Arginate; Chromium Chloride; Chromium Dinicotinate/Glycinate; Chromium Picolinate; Chromium Nicotinate; Chromium Trit; Chromium Yeast; Chromium Nicotinate/Glycinate; Copper Amino Acid Chelate; Copper Aspartate; Copper Carbonate; Copper Citrate; Copper Gluconate; Copper Bis-Glycinate; Copper Glycinate; Copper Sulfate; Copper Yeast; Iron Amino Acid Chelate; Iron Aspartate; Iron Bis-Glycinate HCl Soluble; Iron Citrate; Iron Fumarate; Iron Gluconate; Iron Glycinate; Iron Sulfate; Iron Yeast; Lithium Aspartate; Lithium Orotate; Magnesium Alphaketoglutarate; Magnesium Amino Acid Chelate; Magnesium Ascorbate; Magnesium Aspartate; Magnesium Citrate; Magnesium Gluconate; Magnesium Glycinate; Magnesium Malate; Magnesium Orotate; Magnesium Oxide; Magnesium Succinate; Magnesium Taurinate; Magnesium Yeast; Manganese Amino Acid Chelate; Manganese Aspartate; Manganese Carbonate; Manganese Citrate; Manganese Gluconate; Mananese Glycinate; Manganese Sulfate; Manganese Yeast; Molybdenum Amino Acid Chelate; Molybdenum Trit; Molybdenum Yeast; Sodium Molybdate; Phosphorus Amino Acid Chelate; Dicalcium Phosphate; Potassium Amino Acid Chelate; Potassium Ascorbate; Potassium Aspartate; Potassium Citrate; Potassium Chloride; Potassium D-Glucarate; Potassium Gluconate; Potassium Glycerophosphate; Potassium Iodide Trit; Potassium Succinate; Selenium Amino Acid Chelate; Selenium Aspartate; L-Selenomethionine; Selenium Yeast; Sodium Selenate; Sodium Selenite; Strontium Aspartate; Strontium Citrate; Strontium Glycinate; Vanadium Amino Acid Chelate; Vanadium Citrate; Bis-Maltolato Oxo Vanadium; Vanadyl Sulfate; Sodium Metavanadate; Zinc Acetate; Zinc Arginate; Zinc Amino Acid Chelate; Zinc Ascorbate; Zinc Aspartate; Zinc Gluconate; Zinc Bis-Glycinate; Zinc Glycinate; Zinc Methionate; Zinc Oxide; Zinc Picolinate; Zinc Sulfate; and Zinc Yeast and mixtures thereof.
 3. The composition of claim 1, wherein the amino acid metal chelate is selected from the group consisting of copper bis-glycinate and zinc bis-glycinate.
 4. A method of reducing hydrogen sulfide emission from asphalt or from the preparation of asphalt, comprising the step of: (i) combining an amino acid metal chelate to asphalt or asphalt mix
 5. The method of claim 4 wherein the amino acid metal chelate is selected from the group consisting of Boron Amino Acid Chelate; Boron Aspartate; Boron Citrate; Boron Glycinate; Calcium Alphaketoglutarate; Calcium Amino Acid Chelate; Calcium Arginate; Calcium Ascorbate; Calcium Aspartate; Calcium Caprylate; Calcium Carbonate; Calcium Citrate Malate; Calcium Glycinate; Calcium D-Glucarate; Calcium Krebs Cycle; Calcium Lactate; Calcium Malate; Calcium Orotate; Calcium Succinate; Chromium Amino Acid Chelate; Chromium Arginate; Chromium Chloride; Chromium Dinicotinate/Glycinate; Chromium Picolinate; Chromium Nicotinate; Chromium Trit; Chromium Yeast; Chromium Nicotinate/Glycinate; Copper Amino Acid Chelate; Copper Aspartate; Copper Carbonate; Copper Citrate; Copper Gluconate; Copper Bis-Glycinate; Copper Glycinate; Copper Sulfate; Copper Yeast; Iron Amino Acid Chelate; Iron Aspartate; Iron Bis-Glycinate HCl Soluble; Iron Citrate; Iron Fumarate; Iron Gluconate; Iron Glycinate; Iron Sulfate; Iron Yeast; Lithium Aspartate; Lithium Orotate; Magnesium Alphaketoglutarate; Magnesium Amino Acid Chelate; Magnesium Ascorbate; Magnesium Aspartate; Magnesium Citrate; Magnesium Gluconate; Magnesium Glycinate; Magnesium Malate; Magnesium Orotate; Magnesium Oxide; Magnesium Succinate; Magnesium Taurinate; Magnesium Yeast; Manganese Amino Acid Chelate; Manganese Aspartate; Manganese Carbonate; Manganese Citrate; Manganese Gluconate; Mananese Glycinate; Manganese Sulfate; Manganese Yeast; Molybdenum Amino Acid Chelate; Molybdenum Trit; Molybdenum Yeast; Sodium Molybdate; Phosphorus Amino Acid Chelate; Dicalcium Phosphate; Potassium Amino Acid Chelate; Potassium Ascorbate; Potassium Aspartate; Potassium Citrate; Potassium Chloride; Potassium D-Glucarate; Potassium Gluconate; Potassium Glycerophosphate; Potassium Iodide Trit; Potassium Succinate; Selenium Amino Acid Chelate; Selenium Aspartate; L-Selenomethionine; Selenium Yeast; Sodium Selenate; Sodium Selenite; Strontium Aspartate; Strontium Citrate; Strontium Glycinate; Vanadium Amino Acid Chelate; Vanadium Citrate; Bis-Maltolato Oxo Vanadium; Vanadyl Sulfate; Sodium Metavanadate; Zinc Acetate; Zinc Arginate; Zinc Amino Acid Chelate; Zinc Ascorbate; Zinc Aspartate; Zinc Gluconate; Zinc Bis-Glycinate; Zinc Glycinate; Zinc Methionate; Zinc Oxide; Zinc Picolinate; Zinc Sulfate; and Zinc Yeast and mixtures thereof.
 6. The method of claim 4, wherein the amino acid metal chelate is selected from the group consisting of copper bis-glycinate and zinc bis-glycinate. 